Aciers inoxydables super duplexoffrent une résistance et une résistance à la corrosion bien supérieures à celles du 316. Par conséquent, la réponse immédiate est oui : le super duplex est meilleur que le 316.316.
'Duplex' stainless steels are a family of stainless steels that contain a mixed microstructure of austenite and ferrite phases. They offer a combination of good corrosion resistance and high strength, making them suitable for a wide range of applications. Super duplex stainless steels have a higher content of alloying elements, such as chromium, nickel, and molybdenum, compared to duplex stainless steels. They are based upon 25% chromium content. As such, super duplex stainless steels have up to four times the tensile strength of 316 stainless steel, and considerably better corrosion resistance. An alloys resistance to pitting corrosion can be usefully summarised by the PREN value, which is the 'Pitting Resistance Equivalent number'. The PREN for super duplex stainless steels is >40, contre 316 sur 25 au PREN.
Cependant, malgré les avantages très intéressants des aciers inoxydables super duplex par rapport au 316, il existe certaines limites. Les aciers inoxydables super duplex perdent une grande partie de leur résistance aux chocs en dessous de -50degC, alors que pour le 316, la résistance aux chocs est largement conservée jusqu'aux températures cryogéniques. Les aciers inoxydables super duplex sont limités à des températures de fonctionnement à long terme inférieures à 250 °C, tandis que le 316 peut être utilisé jusqu'à 870 °C (à condition qu'il s'agisse d'un acier à faible teneur en carbone).316Lou variantes 316Ti stabilisées au titane pour éviter la corrosion intergranulaire).
Les aciers inoxydables super duplex sont certainement plus difficiles à usiner, compte tenu de leur résistance beaucoup plus élevée. Ils sont perçus comme plus difficiles à souder mais peuvent être facilement fabriqués avec l'équipement et les procédures appropriés.